Al2O3 |
10.78 |
0.09 |
Mass fraction (10 -2 ) |
|
SiO2 |
67.21 |
0.40 |
Mass fraction (10 -2 ) |
|
As |
9.8 |
0.9 |
Mass fraction (10 -6 sup>) |
|
B |
(51) |
|
Mass fraction (10 -6 sup>) |
|
Ba |
469 |
23 |
Mass fraction (10 -6 sup>) |
|
Be |
2.0 |
0.3 |
Mass fraction (10 -6 sup>) |
|
Bi |
(0.20) |
|
Mass fraction (10 -6 sup>) |
|
Cd |
(0.22) |
|
Mass fraction (10 -6 sup>) |
|
Cl |
600 |
42 |
Mass fraction (10 -6 sup>) |
|
Co |
9.4 |
1.4 |
Mass fraction (10 -6 sup>) |
|
Cr |
61 |
5 |
Mass fraction (10 -6 sup>) |
|
Dy |
17 |
1 |
Mass fraction (10 -6 sup>) |
|
F |
(414) |
|
Mass fraction (10 -6 sup>) |
|
Ga |
12 |
2 |
Mass fraction (10 -6 sup>) |
|
Hg |
0.031×1000 |
0.005 |
Mass fraction (10-9) |
|
La |
36 |
5 |
Mass fraction (10 -6 sup>) |
|
Li |
27 |
2 |
Mass fraction (10 -6 sup>) |
|
Mo |
(0.94) |
|
Mass fraction (10 -6 sup>) |
|
Nb |
12 |
1 |
Mass fraction (10 -6 sup>) |
|
Ni |
23 |
2 |
Mass fraction (10 -6 sup>) |
|
Pb |
21 |
5 |
Mass fraction (10 -6 sup>) |
|
Rb |
86 |
10 |
Mass fraction (10 -6 sup>) |
|
Sb(T) |
0.84 |
0.18 |
Mass fraction (10 -6 sup>) |
|
Se |
0.14 |
0.04 |
Mass fraction (10 -6 sup>) |
|
Sn |
2.9 |
0.6 |
Mass fraction (10 -6 sup>) |
|
Sr |
227 |
7 |
Mass fraction (10 -6 sup>) |
|
Te |
(0.039) |
|
Mass fraction (10 -6 sup>) |
|
Th |
9.6 |
1.2 |
Mass fraction (10 -6 sup>) |
|
U |
1.9 |
0.4 |
Mass fraction (10 -6 sup>) |
|
V |
63 |
4 |
Mass fraction (10 -6 sup>) |
|
W |
1.5 |
0.1 |
Mass fraction (10 -6 sup>) |
|
Y |
21 |
4 |
Mass fraction (10 -6 sup>) |
|
Zn |
51 |
6 |
Mass fraction (10 -6 sup>) |
|
Zr |
291 |
21 |
Mass fraction (10 -6 sup>) |
|
Fe2O3 |
2.28 |
0.14 |
Mass fraction (10 -2 ) |
|
TFe2O3 |
(3.46) |
|
Mass fraction (10 -2 ) |
|
FeO |
(1.06) |
|
Mass fraction (10 -2 ) |
|
CaO |
5.21 |
0.05 |
Mass fraction (10 -2 ) |
|
MgO |
1.73 |
0.15 |
Mass fraction (10 -2 ) |
|
K2O |
2.5 |
0.04 |
Mass fraction (10 -2 ) |
|
N |
0.064 |
0.006 |
Mass fraction (10 -2 ) |
|
S |
340 |
40 |
Mass fraction (10 -6 sup>) |
|
H2O+ |
2.29 |
0.14 |
Mass fraction (10 -2 ) |
|
CO2 |
3.48 |
0.21 |
Mass fraction (10 -2 ) |
|